TPU98A 1.75mm Black 500g
Indicated wieght: actual amount of printable material.
30,00 € VAT exc.
TPU98A is a specifically formulated flexible filament for easy & high speed printing on both direct and Bowden style 3D printers. TPU98A features an exceptionally high heat resistance (138℃) and can be stretched as far as 450% before reaching its breaking point. TPU98A does not require the use of a heated bed and can even be printed straight onto (clean) glass. TPU98A is the flexible filament for (semi)professional users who do not want to compromise and require a high mechanical flexible filament that prints easily. TPU98A is an extremely usable flex-filament with a wide variety of different applications such as Orthopedic insoles, Prosthetics, Vibration dampers and many more.
- Strong & Flexible
- Works on Direct & Bowden style 3D printers
- Printable at speeds of >75mm/s
- Exceptionally high softening point of 138℃
- 450% elongation at break
- Resistance to oils, greases
- Easily printed water-tight
Dimensions
|
Size |
Ø tolerence |
Roundness |
|
1,75mm |
± 0,05mm |
≥ 95% |
|
2,85mm |
± 0,10mm |
≥ 95% |
Physical properties
|
Description |
Méthode test |
Valeur type |
|
Specific gravity |
ISO 1183 |
1,16g/cc |
|
Tensile strength at yeld |
ISO 527 |
50MPa |
|
Strain at break |
ISO 527 |
450% |
|
Tensile modulus |
ISO 527 |
150MPa |
|
Impact strength – Charpy method 23°C |
ISO 179 |
N.B. |
|
Shore hardness |
ISO 7619-1 |
98A |
Thermal properties
|
Description |
Méthode test |
Valeur type |
|
Printing temp. |
- |
235±10˚C |
|
Melting temp. |
ISO 294 |
225°C |
|
Glass transition |
DSC |
-16°C |
|
Vicat softening temp. |
ASTM D1525 |
138% |